Metallurgy is a domain of materials science that studies the physical and chemical behavior of metallic elements, their intermetallic compounds, and their mixtures, which are called alloys. It is also the technology of metals: the way in which science is applied to their practical use. Metallurgy is commonly used in the craft of metalworking.

History

The first evidence of human metallurgy dates from the 5th and 6th millennium BC, and was found in the archaeological sites of Majdanpek, Yarmovac and Plocnik, Serbia. To date, the earliest copper smelting is found at the Belovode site,^[1] these examples include a copper axe from 5,500BC belonging to the Vincha culture.^[2] Other signs of human metallurgy are found from the third millennium BC in places like Palmela (Portugal), Cortes de Navarra (Spain), and Stonehenge (United Kingdom). However, as often happens with the study of prehistoric times, the ultimate beginnings cannot be clearly defined and new discoveries are continuous and ongoing.

Silver, copper, tin and meteoric iron can also be found native, allowing a limited amount of metalworking in early cultures. Egyptian weapons made from meteoric iron in about 3000 B.C. were highly prized as "Daggers from Heaven".^[3] However, by learning to get copper and tin by heating rocks and combining those two metals to make an alloy called bronze, the technology of metallurgy began about 3500 B.C. with the Bronze Age.

The extraction of iron from its ore into a workable metal is much more difficult. It appears to have been invented by the Hittites in about 1200 B.C., beginning the Iron Age. The secret of extracting and working iron was a key factor in the success of the Philistines.^[3][4]

Historical developments in ferrous metallurgy can be found in a wide variety of past cultures and civilizations. This includes the ancient and medieval kingdoms and empires of the Middle East and Near East, ancient Egypt, ancient Nubia, and Anatolia (Turkey), Ancient Nok, Carthage, the Greeks and Romans of ancient Europe, medieval Europe, ancient and medieval China, ancient and medieval India, ancient and medieval Japan, etc. Of interest to note is that many applications, practices, and devices associated or involved in metallurgy were possibly established in ancient China before Europeans mastered these crafts (such as the innovation of the blast furnace, cast iron, steel).^[5] However, modern research suggests that Roman technology was far more sophisticated than hitherto supposed, especially in mining methods, metal extraction and forging. They were, for example, expert in hydraulic mining methods well before the Chinese, or any other civilization of the time.^{[citation needed]}

A 16th century book by Georg Agricola called De re metallica describes the highly developed and complex processes of mining metal ores, metal extraction and metallurgy of the time. Agricola has been described as the "father of metallurgy".^[6]

Extraction

Extractive metallurgy is the practice of removing valuable metals from an ore and refining the extracted raw metals into a purer form. In order to convert a metal oxide or sulfide to a purer metal, the ore must be reduced physically, chemically, or electrolytically.

Extractive metallurgists are interested in three primary streams: feed, concentrate (valuable metal oxide/sulfide), and tailings (waste). After mining, large pieces of the ore feed are broken through crushing and/or grinding in order to obtain particles small enough where each particle is either mostly valuable or mostly waste. Concentrating the particles of value in a form supporting separation enables the desired metal to be removed from waste products.

Mining may not be necessary if the ore body and physical environment are conducive to leaching. Leaching dissolves minerals in an ore body and results in an enriched solution. The solution is collected and processed to extract valuable metals.

Ore bodies often contain more than one valuable metal. Tailings of a previous process may be used as a feed in another process to extract a secondary product from the original ore. Additionally, a concentrate may contain more than one valuable metal. That concentrate would then be processed to separate the valuable metals into individual constituents.

Alloys

Common engineering metals include aluminium, chromium, copper, iron, magnesium, nickel, titanium and zinc. These are most often used as alloys. Much effort has been placed on understanding the iron-carbon alloy system, which includes steels and cast irons. Plain carbon steels are used in low cost, high strength applications where weight and corrosion are not a problem. Cast irons, including ductile iron are also part of the iron-carbon system.

Stainless steel or galvanized steel are used where resistance to corrosion is important. Aluminium alloys and magnesium alloys are used for applications where strength and lightness are required.

Copper-nickel alloys (such as Monel) are used in highly corrosive environments and for non-magnetic applications. Nickel-based superalloys like Inconel are used in high temperature applications such as turbochargers, pressure vessel, and heat exchangers. For extremely high temperatures, single crystal alloys are used to minimize creep.

Production

In production engineering, metallurgy is concerned with the production of metallic components for use in consumer or engineering products. This involves the production of alloys, the shaping, the heat treatment and the surface treatment of the product. The task of the metallurgist is to achieve balance between material properties such as cost, weight, strength, toughness, hardness, corrosion and fatigue resistance, and performance in temperature extremes. To achieve this goal, the operating environment must be carefully considered. In a saltwater environment, ferrous metals and some aluminium alloys corrode quickly. Metals exposed to cold or cryogenic conditions may endure a ductile to brittle transition and lose their toughness, becoming more brittle and prone to cracking. Metals under continual cyclic loading can suffer from metal fatigue. Metals under constant stress at elevated temperatures can creep.

Metalworking processes

Metals are shaped by processes such as:

• casting - molten metal is poured into a shaped mould.
• forging - a red-hot billet is hammered into shape.
• flow forming
• rolling - a billet is passed through successively narrower rollers to create a sheet.
• extrusion - a hot and malleable metal is forced under pressure through a die, which shapes it before it cools.
• sintering - a powdered metal is heated in a non-oxidizing environment after being compressed into a die.
• metalworking
• machining - lathes, milling machines, and drills cut the cold metal to shape.
• fabrication - sheets of metal are cut with guillotines or gas cutters and bent into shape.

Cold working processes, where the product’s shape is altered by rolling, fabrication or other processes while the product is cold, can increase the strength of the product by a process called work hardening. Work hardening creates microscopic defects in the metal, which resist further changes of shape.

Various forms of casting exist in industry and academia. These include sand casting, investment casting (also called the “lost wax process”), die casting and continuous casting.

Heat treatment

Metals can be heat treated to alter the properties of strength, ductility, toughness, hardness or resistance to corrosion. Common heat treatment processes include annealing, precipitation strengthening, quenching, and tempering. The annealing process softens the metal by allowing recovery of cold work and grain growth. Quenching can be used to harden alloy steels, or in precipitation hardenable alloys, to trap dissolved solute atoms in solution. Tempering will cause the dissolved alloying elements to precipitate, or in the case of quenched steels, improve impact strength and ductile properties.

Often, mechanical and thermal treatments are combined in what is known as thermo-mechanical treatments for better properties and more efficient processing of materials. These processes are common to high alloy special steels, super alloys and titanium alloys.

Plating

Electroplating is a common surface-treatment technique. It involves bonding a thin layer of another metal such as gold, silver, chromium or zinc to the surface of the product. It is used to reduce corrosion as well as to improve the product's aesthetic appearance.

Thermal spraying

Thermal spraying techniques are another popular finishing option, and often have better high temperature properties than electroplated coatings.

Microstructure

Metallurgists study the microscopic and macroscopic properties using metallography, a technique invented by Henry Clifton Sorby. In metallography, an alloy of interest is ground flat and polished to a mirror finish. The sample can then be etched to reveal the microstructure and macrostructure of the metal. The sample is then examined in an optical or electron microscope, and the image contrast provides details on the composition, mechanical properties, and processing history.

Crystallography, often using diffraction of x-rays or electrons, is another valuable tool available to the modern metallurgist. Crystallography allows identification of unknown materials and reveals the crystal structure of the sample. Quantitative crystallography can be used to calculate the amount of phases present as well as the degree of strain to which a sample has been subjected.

See also

• Metallurgical failure analysis
• Archaeometallurgy
• CALPHAD
• Carbonyl metallurgy
• Cupellation
• Georg Agricola
• Goldbeating
• Mineral industry
• National Institute of Foundry and Forge Technology
• Pyrometallurgy
• Timeline of materials technology

References

af:Metaalkunde ar:علم الفلزات an:Metalurchia az:Metallurgiya bn:ধাতুবিদ্যা be:Металургія be-x-old:Мэталюргія bs:Metalurgija bg:Металургия ca:Metal·lúrgia cs:Metalurgie da:Metallurgi de:Metallurgie et:Metallurgia el:Μεταλλουργία es:Metalurgia eo:Metalurgio eu:Metalurgia fa:متالورژی fr:Métallurgie gl:Metalurxia gan:冶金學 ko:금속 공학 hi:धातुकर्म hr:Metalurgija id:Metalurgi is:Málmfræði it:Metallurgia he:מטלורגיה kn:ಲೋಹಶಾಸ್ತ್ರ la:Metallurgia lt:Metalurgija hu:Kohászat ms:Metalurgi mwl:Metalurgie nl:Metallurgie ja:金属工学 no:Metallurgi pl:Metalurgia pt:Metalurgia ro:Metalurgie qu:Q'illay llamk'ay ru:Металлургия scn:Mitallurgia simple:Metallurgy sk:Metalurgia sl:Metalurgija sr:Металургија sh:Metalurgija fi:Metallurgia sv:Metallurgi tl:Metalurhiya ta:உலோகவியல் th:วิศวกรรมโลหการ tr:Metalurji uk:Металургія vi:Luyện kim fiu-vro:Metallurgia war:Metalurhiya zh-yue:冶金學 diq:Metallurciye

1. ↑ doi:10.1016/j.jas.2010.06.012
2. ↑ Neolithic Vinca was a metallurgical culture Stonepages from news sources November 2007
3. ↑ ^{3.0 3.1} W. Keller (1963) The Bible as History page 156 ISBN 0 340 00312 X
4. ↑ B. W. Anderson (1975) The Living World of the Old Testament page 154 ISBN 0-582-48598-3
5. ↑ R. F. Tylecote (1992) A History of Metallurgy ISBN 0-901462-88-8
6. ↑ Karl Alfred von Zittel (1901) History of Geology and Palaeontology page 15